E matuā maualalo lava le fa'alauteleina o le vevela o le tioata borosilicate, e tusa ma le tasi o tioata soda lime e tolu. O mea autū e aofia ai o le 59.6% oneone silica, 21.5% boric oxide, 14.4% potassium oxide, 2.3% zinc oxide ma sina vaega itiiti o le calcium oxide ma le aluminium oxide.
E te iloa nisi uiga?
| Mafiafia | 2.30g/cm² |
| Faigata | 6.0′ |
| Modulus o le Elasticity | 67KNmm – 2 |
| Malosiaga o le Fetaia'i | 40 – 120Nmm – 2 |
| Fua Fa'atatau o le Poisson | 0.18 |
| Fa'atusatusaga o le Fa'alauteleina o le Vevela 20-400°C | (3.3)*10`-6 |
| Fa'atinoina o le Vevela Fa'apitoa 90°C | 1.2W*(M*K`-1) |
| Fa'asinomaga Fa'ata'ita'i | 1.6375 |
| Vevela Fa'apitoa | 830 J/KG |
| Tulaga e liusuavai ai | 1320°C |
| Tulaga Fa'amalūlūina | 815°C |
| Te'i Fa'avevela | ≤350°C |
| Malosiaga o le A'afiaga | ≥7J |
| Onosa'i i le Vai | HGB 1级 （HGB 1) |
| Tete'e atu i le 'Aseta | HGB 1级 （HGB 1) |
| Tete'e atu i le Alkali | HGB 2级 （HGB 2) |
| Meatotino e Tetee Atu i le Mamafa | ≤10Mpa |
| Tete'e i le Leo | 1015Ωcm |
| Fa'aauau pea o le Dielectric | 4.6 |
| Malosiaga Dielectric | 30 kV/mm |
Ua lauiloa i lona tete'e atu i le vevela ma le tumau faaletino,tioata borosilicatee faʻaaogaina i le tele o ituaiga o alamanuia ma talosaga.
– Meafaigaluega Tioata i le Fale Su'esu'e
— Paipa Tioata Fa'afoma'i
— Meafaigaluega mo le kuka ma le umukuka
— Meafaigaluega Va'ai
— Teuteuga Moli
— Ipu inu ma isi mea faapena.
O Saida Glass o se tagata tomai faapitoaFA'AGALUEGA O TIOATAfalegaosimea e silia ma le 10 tausaga, taumafai e avea ma falegaosimea pito i luga e 10 ma ofoina atu ituaiga eseese o mea faʻapitoatioata, e pei o le tioata ufiufi mai le 7'' i le 120'' mo so'o se fa'aaliga, paipa tioata borosilicate 3.3 mai le la'ititi o le OD lautele. 5mm i le maualuga o le OD lautele. 315mm.
Saida GlassE taumafai pea lava pea e avea ma au paaga faatuatuaina ma tuu atu ia te oe e lagonaina le taua o auaunaga faaopoopo.
Taimi na lafoina ai: Aokuso-13-2020