Ingilazi ye-borosilicate inokukhula okuphansi kakhulu kokushisa, cishe eyodwa kwezintathu zengilazi ye-soda lime. Izinhlanganisela eziyinhloko ezilinganiselwe ziyi-59.6% yesihlabathi se-silica, i-21.5% ye-boric oxide, i-14.4% ye-potassium oxide, i-2.3% ye-zinc oxide kanye namanani amancane e-calcium oxide kanye ne-aluminium oxide.
Uyazi ukuthi yiziphi ezinye izici?
| Ubuningi | 2.30g/cm² |
| Ubulukhuni | 6.0′ |
| I-Elasticity Modulus | 67KNmm – 2 |
| Amandla Okudonsa | 40 – 120Nmm – 2 |
| Isilinganiso se-Poisson | 0.18 |
| Isilinganiso Sokwanda Kokushisa 20-400°C | (3.3)*10`-6 |
| Ukushisa Okuqondile 90°C | 1.2W*(M*K`-1) |
| Inkomba Yokubukeza | 1.6375 |
| Ukushisa Okuqondile | 830 J/KG |
| Indawo Yokuncibilika | 1320°C |
| Indawo Yokuthambisa | 815°C |
| Ukushaqeka Okushisayo | ≤350°C |
| Amandla Omthelela | ≥7J |
| Ukubekezelelana Kwamanzi | I-HGB 1级 (HGB 1) |
| Ukumelana ne-asidi | I-HGB 1级 (HGB 1) |
| Ukumelana ne-Alkali | I-HGB 2级 (HGB 2) |
| Izakhiwo Ezimelana Nokucindezela | ≤10Mpa |
| Ukumelana Nomthamo | 1015Ωcm |
| I-Dielectric Constant | 4.6 |
| Amandla e-Dielectric | 30 kV/mm |
Yaziwa ngokumelana nokushisa kwayo nokuqina kwayo ngokomzimba,ingilazi ye-borosilicateisetshenziswa ezimbonini eziningi kanye nezicelo ezahlukahlukene.
- Izingilazi Zelebhu
— Amapayipi Engilazi Ezemithi
— Izitsha Zokupheka Nezinto Zasekhishini
— Imishini Yokubona
— Umhlobiso Wokukhanyisa
— Izingilazi zokuphuza njll.
USaida Glass unguchwephesheUKUCubungulwa KWENGILASIifektri engaphezu kweminyaka eyi-10, lwela ukuba yizimboni eziyi-10 eziphezulu ezinikeza izinhlobo ezahlukene zemikhiqizo eyenziwe ngokwezifisoingilazi, njengengilazi yokumboza kusukela ku-7'' kuya ku-120'' kunoma yisiphi isibonisi, amashubhu engilazi e-borosilicate angu-3.3 kusukela ku-min. OD dia. 5mm kuya ku-max. OD dia. 315mm.
Ingilazi kaSaidauhlala elwela ukuba ngumlingani wakho othembekile futhi akuvumele uzizwele izinsizakalo eziwusizo.
Isikhathi sokuthunyelwe: Agasti-13-2020