Iko Borosilicate nwere mgbasawanye ọkụ dị ala, ihe dị ka otu n'ime iko soda lime atọ. Ihe mejupụtara ya bụ 59.6% silica ájá, 21.5% boric oxide, 14.4% potassium oxide, 2.3% zinc oxide na ọnụọgụ calcium oxide na aluminum oxide.
Ị maara àgwà ndị ọzọ?
| Njupụta | 2.30g / cm² |
| Isi ike | 6.0′ |
| Elasticity Modul | 67KNmm - 2 |
| Ike ọdụdọ | 40 - 120Nmm - 2 |
| Oke Poisson | 0.18 |
| Ọnụọgụ nke Mgbasa ọkụ 20-400°C | (3.3) * 10`-6 |
| Okpomọkụ a kapịrị ọnụ 90°C | 1.2W*(M*K`-1) |
| Ntụgharị uche | 1.6375 |
| Okpomọkụ akọwapụtara | 830 J/KG |
| Ebe mgbaze | 1320C |
| Ebe Ntụcha | 815°C |
| Igwe ọkụ ọkụ | ≤350C |
| Mmetụta Mmetụta | ≥7J |
| Nkwenye mmiri | HGB 1 (HGB 1) |
| Acid na-eguzogide | HGB 1 (HGB 1) |
| Nguzogide Alkali | HGB 2 maka (HGB 2) |
| Njirimara na-eguzogide nrụgide | ≤10Mpa |
| Mgbochi olu | 1015Ωcm |
| Dielectric Constant | 4.6 |
| Ike Dielectric | 30 kV / mm |
Amara maka nguzogide okpomọkụ na ịdịte aka anụ ahụ.iko borosilicatea na-eji ya na ụlọ ọrụ na ngwa dị iche iche.
– Laboratory Glassware
- Igwe mmiri iko ọgwụ ọgwụ
- Ngwa ngwa nri na kichin
- Ngwa ngwa anya
- Ihe ịchọ mma ọkụ
- Igwe ihe ọṅụṅụ wdg.